Copolymerization of Chloroprene with Methyl Methacrylate by the Et _n AICI ₃ . _n (n=1, 1.5, 2)-Vanadium Compound System

Abstract

Abstract The copolymerization of chloroprene with methyl methacrylate was studied in the presence of Etn A1C13-n (n=1, 1.5, 2)-vanadium compounds. Monomer reactivity ratios in various catalyst concentrations were compared with that of a usual radical initiator. The apparent monomer reactivity ratio changed with the concentration of alkylaluminum halide. In this polymerization, alternating copolymer could not be prepared by the ordinary catalyst concentration by which the alternating copolymerization of chloroprene with acrylonitrile was carried out. The addition of more than 10 mole % of the alkylaluminum halide based on two monomers was required to prepare the copolymer which had equimolar composition irrespective of the feed monomer ratio. The configuration in the repeating unit of the copolymer was discussed by comparison with the NMR and IR spectra of the radical copolymer and the cyclic Diels-Alder adduct of chloroprene-methyl methacrylate. The high alternating tendency was clarified by ozonolysis of the copolymer which was prepared under the conditions which produced equimolar copolymer in various feed monomer ratios. The chloroprene unit of the copolymer was present in the 1, 4-trans structure in the copolymer prepared by the Etn A1C13-n -vanadium compound system.