High‐Mobility, Aligned Crystalline Domains of TIPS‐Pentacene with Metastable Polymorphs Through Lateral Confinement of Crystal Growth

Abstract

Patterns composed of solvent wetting and dewetting regions promote lateral confinement of solution-sheared and lattice-strained TIPS-pentacene crystals. This lateral confinement causes aligned crystal growth, and the smallest patterns of 0.5 μm wide solvent wetting regions promotes formation of highly strained, aligned, and single-crystalline TIPS-pentacene regions with mobility as high as 2.7 cm(2) V(-1) s(-1) .