Influences of Y Addition on Mechanical Properties and Oxidation Resistance of CrN Coating

Abstract

Abstract Cr 1-x Y x N coatings were fabricated by reactive co-sputtering deposition and the Y content was changed by varying the Y target power. The influence of varying amounts of Y addition on the mechanical properties and oxidation resistance of CrN coatings has been studied. The results reveal that Y ions substitute Cr ions in Cr-N lattice forming the solid solution Cr 1-x Y x N coatings. Y doping has a beneficial effect on the improvements of hardness and adhesion of the coatings. After the oxidation in air at 850 °C for 2 h, The CrN coating with 1.2 at. % Y addition exhibits superior oxidation resistance than Y-free CrN coating, while over doping of Y produces detrimental effects on oxidation resistance of the coatings.