Corrosion of AISI 304 stainless steel induced by thermophilic sulfate reducing bacteria (SRB) from a geothermal power unit

Abstract

Corrosion behavior of AISI 304 stainless steel induced by two strains of thermophilic sulfate reducing bacteria (SRB) was analyzed. Inoculated bacteria were isolated from the surface condenser's tubes of “Los Azufres”, a geothermal electric field located in the State of Michoacan in Central Mexico. Anaerobic corrosion tests were carried out for two months in Czapek's medium at 50°C and 90°C inoculated with strains. The examination in scanning electron microscope (SEM) was accomplished to determine the type of corrosion, morphology, and preferential attacked zones. Measuring the corrosion potential and determining of anodic potentiodynamic polarization curves after two months of exposure in anaerobic conditions carried out an electrochemical study. Durch thermophile sulfatreduzierende Bakterien aus einem geothermischen Kraftwerk induzierte Korrosion von nichtrostendem Stahl 1.4301 Das durch zwei Arten thermophiler sulfatreduzierender Bakterien (SRB) induzierte Korrosionsverhalten von nichtrostendem Stahl 1.4301 wurde untersucht. Geimpfte Bakterien wurden von der Oberfläche der Verdampferrohre von „Los Azufres”︁, einem geothermischen, elektrischen Feld im Staat Michoacan in Zentralmexiko, isoliert. Anaerobe Korrosionsprüfungen wurden über zwei Monate in Czapeks-Medium, das mit den zwei Arten geimpft war, bei 50 und 90°C durchgeführt. Die Untersuchungen im Rasterelektronenmikroskop wurden vorgenommen, um die Art der Korrosion, die Morphologie und die bevorzugt angegriffenen Bereiche zu ermitteln. Die elektrochemischen Untersuchungen beinhalteten die Messung des Korrosionspotentials und die Ermittlung anodischer potentiodynamischer Polarisationskurven nach zweimonatiger Auslagerung.