Influence of aggregation, defects, and contaminant oxygen on water dissociation at Cu(110) surface: A theoretical study

Abstract

The DFT-PW91 slab model approach is employed to investigate the influence of aggregation, surface defects, and contaminant oxygen on water dissociation on Cu(110) at low temperatures. The dissociation barriers of water in various aggregate states are calculated in the range of 60-75 kJ/mol on the clean surfaces, in nice agreement with the experimentally determined values. It is revealed that the aggregation of water shows no propensity to reduce the activation barrier for the O-H bond breaking on Cu(110), at variance with the water chemistry on Ru(0001). The calculated activation energy on Cu(211) which is the most active stepped surface investigated is equal to the value on the (110) surface, indicating that the hydroxyl groups observed on Cu(110) at low temperatures may not stem from surface defects. The coadsorbed oxygen, whether as a "spectator" or a "participant," facilitates the water dissociation both kinetically and thermodynamically.