Natural SciencesMaterials EngineeringMaterials ScienceCondensed Matter PhysicsMetallic MaterialsMetallurgyAlloysMetalsPrecipitationPrecipitation FormationPrecipitation ProcessesThermodynamics Of Precipitation FormationIntermetallic PrecipitationPrecipitation EquilibriaPrecipitation HardeningPrecipitation KineticsPrecipitation Thermodynamics
The precipitation behaviour of Cu−1 at% Co and Cu−3 at% Co alloys under isothermal annealing was investigated. The present TEM and SEM work revealed that a coherent Co-rich precipitate with an octahedral shape surrounded by {110} planes was formed in the ageing process at 600 to 800°C under zero magnetic field. Satellite precipitates were arranged adjacent to the parent large Co-rich precipitates in 〈100〉 directions.