RuO4 staining and lamellar structure of ?- and ?-PP

Abstract

Monoclinic (α) and hexagonal (β) polypropylene (α- and β-PP) were stained in the vapor of a ruthenium tetroxide solution prepared in situ. The effect of staining on the fusion behavior was investigated using a DSC. A staining duration between 10 and 24 h was found suitable for obtaining a good electron contrast between the crystalline and amorphous regions for TEM examination without causing severe damage to the crystals. The spherulites of the water-quenched α-PP were found to be composed of very fine cross-hatched lamellae whose long period was about 10 nm. In comparison, the β-PP spherulites crystallized isothermally at 130°C had a category 2 morphology and the lamellae have a long period of 20 nm. The morphology of the spherulite boundary varied depending on the contact angle between the lamellae of the neighboring spherulites. © 1999 John Wiley & Sons, Inc. J Appl Polym Sci 72: 1529–1538, 1999