The Effect of Stress and TiC Coated Balls on Lifetime of a Perfluoropolyalkylether Using a Vacuum Rolling Contact Tribometer

Abstract

A vacuum spiral orbit tribometer (SOT) was used to determine the relative lifetimes of a branched perfluoropolyalkylether (PFPAE) on 440 C stainless steel. The effect of varying the mean Hertzian stress (0.75, 1.0, 1.5 and 2.0 GPa) and the use of TiC coated balls on lubricant lifetime was studied. Other conditions included: approx. 100 rpm, approx. 50 micro-g of lubricant, an initial vacuum level of less than 1.3 x 10(exp -6) Pa (less than 10 x 10(exp -8) Torr), and room temperature (approx. 23 C). Increasing the mean Hertzian stress from 0.75 to 2.0 GPa results in an exponential decrease in lubricant lifetime for both material combinations. However, substituting a TiC ball for the 440 C ball quadrupled lifetime at low stress levels (0.75 and 1.0 GPa) and doubled life at higher stresses (1.5 and 2.0 GPa), The reduced reactivity of the TiC surface with the PFPAE lubricant is considered to be the reason for this enhancement. Decreasing lifetime with increasing stress levels correlated well with energy dissipation calculations.