Deformation Behavior of Magnesium Single Crystal in <i>c</i>-Axis Compression and <i>a</i>-Axis Tension

Abstract

In general, deformation behavior of magnesium in compression is different from tensile. To investigate deformation behavior of magnesium single crystals by non-basal slips and twins, c-axis compression and a-axis tension tests were performed in the range of 77K-573K. The crystals were yielded by second order pyramidal slip, and the yield stress shows anomalous temperature dependence (increased with increasing temperature) between 203K and 293K. Yield stress of c-axis compression was bigger than that of a-axis tensile. In compression, fracture surface were (11 4) under 293K and were {30 4} above 373K, and fracture strain was smaller than the case of tension test. {10 1}-{10 2} double twin were activated at higher temperature and the crystal, therefore, fractured along the twin interface.