Effects of gauge length and strain rate on fracture toughness of polyethylene terephthalate glycol (PETG) film using the essential work of fracture analysis

Abstract

Abstract Essential Work of Fracture (EWF) analysis was used to study the fracture toughness of a PETG film. In the study of the gauge length ( Z ) effect on the specific essential work ( w e ) using Z = 50, 100, 150, 200 and 250 mm, it is observed that w e is Independent of gauge length, except that a slightly lower w e value was measured for Z = 50 mm. Interestingly, for specimens with long gauge lengths (Z ≥ 150 mm in this study), brittle fracture occurred. The minimum ligament length at which ductile/brittle transition took place was observed to decrease with increasing gauge length. There is a small strain rate effect on w e with loading rates less than 1 mm/min. But with higher loading rates, w e showeld no strain rate sensitivity.