Compressive creep behaviour of Mg–Li–Al alloy

Abstract

The compressive creep behaviour of as cast Mg–14Li–1·3Al (wt-%) alloy was investigated in the temperature range of 20−85°C and under different compressive stress in the range of 37·3–74·6 MPa with special apparatus. Primary creep deformation and steady creep rate increase with temperature and applied stress. The compressive creep behaviour obeys an empirical equation ln t= C− nln σ + Q/ RT, where t is the time to a selected creep strain, σ is the applied stress, T is the absolute temperature, R is the gas constant, and C, n, and Q are constants for the experimental alloy. The average values of the exponent n and the creep activation energy Q are 4·33 and 101·13 kJ mol −1 respectively. The creep rate controlling mechanism is the dislocation climb and the lattice diffusion of Li in the experimental alloy under the testing conditions.