Residual stress measurement in steel plates and welds using critically refracted longitudinal (LCR) waves

Abstract

Abstract The application of acoustoelasticity using critically refracted longitudinal (LCR) waves is described for measuring residual stress in welded steel plates. Residual stresses are self-equilibrating and may exist in a material that has been deformed in a nonhomogeneous manner. When unknown residual stress is present in a structure, the true stress may become significantly greater than the working stress. In a corrosive environment, highly stressed areas that have not been properly stress relieved are prone to stress corrosion cracking. Areas near welds are particularly susceptible to stress corrosion cracking. Two welded plates were investigated for the present work: one hot-rolled and the other cold-rolled. Residual stresses are usually greatest after welding. Further, longitudinal stress (i.e., stress parallel to the weld bead) is typically greater than the component transverse to the weld bead. Since the acoustoelastic behavior of the LCR wave is largest when propagated parallel to a uniaxial st...