Morphology and Damage Mechanisms of the Transcrystalline Interphase in Polypropylene

Abstract

Abstract By coating glass fibers with the appropriate nucleating agent, transcrystallinity can be generated in polypropylene/glass composities. Transcrystallinity can consist either of the alpha (monoclinic) or beta (hexagonal) crystal structure. Through the use of directional solidification, the transcrystalline morphology can be duplicated in polypropylene films on a level large enough for mechanical and morphological study. Permanganic etching and subsequent electron microscopy reveals that lamellar orientation in alpha transcrystallinity differs significantly from the beta form. Alpha transcrystallinity consists of lamellae which are edge-on relative to the polypropylene film thickness, while beta transcrystallinity consists of lamellae which are primarily flat-on. This difference in morphology results in significant variations in mechanical properties and damage mechanisms.