Raman scattering and luminescence of yttria nanopowders and ceramics

Abstract

We have studied Raman scattering in yttria nanopowders and ceramics that was excited by radiation at wavelengths of 514.5 and 632.8 nm. We show that, in undoped nanopowders and cubic phase of doped yttria ceramics, only the Raman scattering by phonons is observed, with no other Raman scattering centers having been revealed. In nanopowders of the monoclinic phase, we have observed an additional Raman line with a Raman shift of 1093 ± 4 cm −1 . If all the objects under investigation are excited by the radiation at a wavelength of 514.5 nm, their spectra exhibit four series of photoluminescence lines, two of which (at λ = 521–523 and 538–564 nm) are emitted by Er 3+ ions, “impurity” dopants, while the other two lines (at λ = 607–635 and 644–684 nm) are emitted by intrinsic centers. Under excitation by the radiation at a wavelength of 632.8 nm, only a series of bands at λ = 644–684 nm is emitted. In addition to these photoluminescence bands, neodymium-doped ceramics show photoluminescence bands of Nd 3+ ions. We have shown that intrinsic luminescence centers, which occur in all the examined specimens, are capable of acting as acceptors with respect to neodymium ions excited to the upper laser level.