Cladding of Tantalum and Niobium on Titanium by Electron Beam, Injected in Atmosphere

Abstract

The aim of the work was to clad Ti-Ta-Nb coating on a substrate of pure titanium. Cladding was carried out by non-vacuum electron-beam treatment. As a result a good quality coating thickness of about 2 mm was obtained. Microstructural and microhardness tests were conducted. Dendritic structure and the borders of the former grains of β-phase were revealed. At the microlevel, the coating has a martensitic structure. The average hardness of coating is about 4000 MPa.