Swelling and mechanical properties of cellulose hydrogels. II. The relation between the degree of swelling and the creep compliance

Abstract

The mechanical properties of swollen cellulose hydrogels have been studied. The degree of swelling of the gels was varied between 0.75 and 6.3 g water/g dry gel (g/g) by partial drying followed by reswelling in water. Creep rate was measured in uniaxial compression in the time interval 15–900 s for gels in equilibrium with water. Isochronous relations between stress and reversible strain were found to be linear, and creep compliance was calculated from the slopes. Both the creep compliance and the creep rate increase with an increased degree of swelling. General observations, such as the high strain limit of linearity in the stress–strain curves and the magnitude of the creep compliance, indicate similarities between swollen cellulose gels and rubbery networks. It is therefore assumed that the statistical theories for swollen networks can describe the amorphous matrix of the gels. In order to obtain creep compliance values representative of the amorphous matrix, the experimental values were corrected for the presence of crystalline regions. It is also suggested that non-load-bearing microvoids are present at high swelling levels. According to calculations based on the theory, the network chains of the amorphous regions in a gel swollen to 2.4 g/g contain about 11 monomer units and the Flory-Huggins interaction parameter χ equals 0.2.