Studies on thermal decomposition and oxidation of CoSb3

Abstract

Thermal durability of CoSb3 in vacuum, helium and air was investigated over the temperature range of 20–850 °C. A scanning electron microscope (SEM) and X-ray powder diffraction technique were used to investigate the microstructure and to carry out the phase analysis of the degradation products. The analysis of a non-isothermal and isothermal decomposition and oxidation of the CoSb3 powders and polycrystalline samples were performed using simultaneous TG/DTA technique. More detailed studies were carried out on the oxidation in the temperature range 400–600 °C. It was established that the decomposition products are CoSb2 and a volatile antimony. In case of oxidation a complex three-layered scale is formed, consisting of CoSb2O4, CoSb2O6 and Sb2O4 layers. Both the decomposition and the oxidation kinetics are determined by a diffusion through the growing layers of products. The electrical resistivity and Seebeck coefficient measurements have been also performed on pure and oxidized samples, which showed a large influence of the oxidation on the electrical properties.