Epitaxial growth of YBa<sub>2</sub>Cu<sub>3</sub>O<sub>7−x</sub> films on Ce<sub>0.9</sub>La<sub>0.1</sub>O<sub>2−y</sub> buffered yttria-stabilized zirconia substrates by an all-chemical-solution route
18
Citations
12
References
2014
Year
Materials ScienceAll-chemical-solution RouteSuperconducting MaterialYttria-stabilized Zirconia SubstrateEngineeringHigh-tc SuperconductivityOxide ElectronicsApplied PhysicsSuperconductivityCondensed Matter PhysicsHigh Tc SuperconductorsYttria-stabilized Zirconia SubstratesAll-chemical Derived ConfigurationThin FilmsEpitaxial Growth
A high critical current density of 3 MA cm<sup>−2</sup> (77 K, self-field) was achieved on a YBa<sub>2</sub>Cu<sub>3</sub>O<sub>7</sub> film deposited on Ce<sub>0.9</sub>La<sub>0.1</sub>O<sub>2</sub> buffered yttria-stabilized zirconia substrate, which is an all-chemical derived configuration.