Time‐dependent visco‐elastic creep and recovery of flowable composites

Abstract

Creep behaviour of flowable composites was evaluated in relation to their filler fraction and the postcure period. Solid cylindrical specimens were prepared (4 x 6 mm) using steel moulds, with thorough light curing from multiple directions at 600 mW cm(-2). The specimens were divided into two groups (n=3/material) as follows: group I, loaded 5 min after preparation; and group II, loaded after storage for 1 month in water at 37+/-1 degrees C. A constant compressive stress of 36 MPa was applied to each specimen for 2 h followed by removal of the weight for 2 h of strain recovery. Axial strain measurements were obtained continuously over the total analysis time of 4 h. The maximum creep strain ranged from 2.04 to 7.69% and from 1.03 to 6.12% for groups I and II, respectively. Flowables that had the highest percentage of filler produced the lowest creep strain. The creep response decreased with 1 month of preload storage. Clinically, the finding of this study suggests that flowable composites are unsuitable for stress-bearing areas.