Influence of chunky graphite on mechanical and fatigue properties of heavy‐section cast iron

Abstract

ABSTRACT This research work aimed to find out the influences of the different amounts of chunky graphite on mechanical and fatigue properties of GJS 800 ductile cast iron. Chunky graphite has been a problem of heavy section thick‐walled ductile cast iron components. Chunky graphite is branched and interconnected as a network within eutectic cells and has been observed to form in thermal centres of heavy ductile cast iron sections during solidification. This research work proved that chunky graphite in the microstructure decreases the ultimate tensile strength, the elongation to fracture and fatigue life significantly, but does not influence on the yield stress of ductile cast iron GJS 800 substantially. Low nodular count and nodularity rate also decrease the fatigue life of ductile cast iron, and the difference of fatigue life of specimens containing chunky graphite or having low nodular count and nodularity rate is not large. Influence of the amount of chunky graphite on fatigue life increases until 20% chunky graphite content, and above that the fatigue life does not decrease substantially.