Emulsion Polymerized Polystyrene/Montmorillonite Nanocomposite and its Viscoelastic Characteristics

Abstract

A novel polystyrene (PS)/clay nanocomposite was synthesized using a simple emulsion polymerization method in the presence of sodium ion exchanged montmorillonite (Na‐MMT). Prior to the radical polymerization procedure with potassium persulfate (KPS) as an initiator, the hydrophobic styrene monomer was intercalated into hydrophilic clay layers using sodium dodecyl sulfate (SDS) as a surfactant. The FTIR spectra of the products showed the characteristic absorbance peaks of both the synthesized PS and Na‐MMT. The x‐ray diffraction patterns of the products exhibited an increase in the d 001‐spacing, pointing to the intercalation of the PS chains into the intergalleries of the Na‐MMT. The enhancement of the thermal properties of the nanocomposite materials, such as the increase in the glass transition temperature of the PS, was investigated by differential scanning calorimetry (DSC). Furthermore, based on the viscoelastic properties of the products examined using a rotational rheometer with a parallel plate geometry, the nanocomposites were found to exhibit more rapid shear thinning and increased storage (G′) and loss (G″) moduli with increasing clay content.