Ferroelectric polarization switching in nylon‐11

Abstract

Abstract Cold‐drawn Nylon‐11 films, which were prepared by stretching the melt‐quenched films to a draw ratio of 2.8: 1 at room temperature, were found to exhibit an electric displacement versus electric field hysteresis loop. The results confirmed that the Nylon‐11 film exhibited ferroelectric behavior at or below room temperature. The coercive fields were 65, 98, 125, 160, and 215 MV/m at 20, 0, −20, −40, and −60°C and the remanent polarization at −20°C (where there was considerably less dc conduction) was 56 mC/m 2 . Switching of the polarization was almost completed within 20 ms.