Monocrystal-Polycrystal Elastic Constants of a Stainless Steel

Abstract

For a face-centered-cubic steel, new measurements of the monocrystal Voigt elastic-stiffness constants C11, C12, C44 are given. The monocrystal steel, Fe19Cr10Ni, corresponds closely to the well-known AISI-304 austenitic stainless steel. Considering seven theories for the monocrystalpolycrystal elastic constants, it is found that the Hershey-Kröner-Eshelby theory agrees best with measurements. It predicts the shear modulus within 2% of observation, where the Voigt-Beuss first-order bounds differ by 49%. Ten sets of FeCrNi Cij results are reviewed with the finding that both Zener's elastic anisotropy and the C12/C11 ratio are constant within 5%. Für kubisch-f lächenzentrierten Stahl werden neue Meßergebnisse der einkristallinen Voigtschen Elastizitätskonstanten: C11Cn, C12O12 und C14 mitgeteilt. Der einkristalline Stahl Fe19Cr10Ni entspricht gut dem bekannten rostfreien Austenitstahl AISI304. Durch Berücksichtigung von sieben Theorien für die einkristallinen-polykristallinen Elastizitätskonstanten wird gefunden, daß die Hershey-Kröner-Eshelby-Theorie am besten mit den Messungen übereinstimmt. Sie sagt den Schermodul innerhalb von 2% zu den Beobachtungen voraus, während die Voigt-Reuss-Sätze erster Ordnung um 49% abweichen. Es werden zehn Sätze von Cij-Ergebnissen in FeCrNi diskutiert und es wird gefunden, daß sowohl die Zenersche elastische Anisotropie als auch das C11/C14-Verhältnis innerhalb 5% konstant sind.