Fracture and fatigue behavior of scrim cloth adhesively bonded joints with and without rivet holes

Abstract

—Tensile and fatigue disbond propagation studies on scrim cloth structural adhesive lap joints without and with rivet holes were performed. The geometry of the rivet holes is similar to that in a fuselage part of an aircraft. The joints were cycled in tension-tension fatigue at a frequency of 3 Hz and a maximum load, below the linear limit of the joint, which was obtained from the tensile tests of similar joints. The disbond length at each corner of the joint was viewed using a travelling optical microscope attached to a video camera. It was found that the static-tensile behavior of both types of joints (without and with rivet holes) consists of three stages: a linear stage followed by a region of increased non-linearity and then a 'yield' region. It is within this yield region that the rivet holes affect the strength of the joint. Stress analysis of the disbond problem under static loading revealed a strong mixed mode between the opening and shear mode stress intensity factors for both types of joints. The fatigue disbond kinetics of adhesively bonded joints without and with rivet holes were found to display an S-shaped curve with three stages of the disbond propagation rate. Failure analysis of the fatigue failed joints (without and with rivet holes) revealed three distinct regions on each half of the failed joint: an interfacial region with bare metal, a cohesive region, and an interfacial region with the adhesive adhered to the substrate. Scanning electron microscopic analysis of the disbond surface showed that the cohesive region of the fatigue fractured joints is more tortuous compared with the statically failed joints.