Improving the field emission of carbon nanotubes by lanthanum-hexaboride nano-particles decoration

Abstract

Field emission of carbon nanotubes (CNTs) was remarkably improved by lanthanum-hexaboride (LaB6) nano-particles (NPs) decoration. CNTs were grown on the silicon substrate by chemical vapor deposition. Field emission of bare CNTs and LaB6-NPs decorated CNTs was carried out under same conditions. Physical, morphological, elemental, and graphitic nature changes were ascertained by scanning electron microscope, transmission electron microscope, energy dispersive x-ray spectroscopy, and Raman analysis. LaB6-NPs decorated CNTs show significant reduction of turn-on electric-field from 3.0 to 2.1 V/μm. A remarkable improvement of more than six-fold from 2.05 to 13.19 mA/cm2 at a field of 4.6 V/μm was also observed in the current-density.