Bond Strength of Different Restorative Materials to Light-Curable Mineral Trioxide Aggregate

Abstract

The analysis of variance that compared the experimental groups revealed the presence of significant differences among the groups (P < 0.001). The highest (19.3 MPa) and the lowest (3.4 MPa) bond strength value were recorded for the MB composite-TheraCal and the GIC-TheraCal, respectively.There were significant differences in bond strength between the TheraCal and the MTA groups for the MB composite subgroup (P < 0.001) and the SB composite subgroup (P < 0.05); however, there was no significant difference in bond strength for the GIC subgroup (P ≯ 0.05). Conlusions: The results from this in vitro study suggest that the new pulp capping material, known as light-curable MTA, showed clinically acceptable and higher shear bond scores compared to MTA when used with the MB composite.