Fabrication of TiB<sub>2</sub>-TiC Composites Optimized by Different Amount of Carbon in the Initial Ti-B-C Powder Mixture

Abstract

Composites of TiC and TiB 2 (TiC-TiB 2 ) were prepared by self-propagating high-temperature synthesis (SHS), using compacted reactant different combinations of Ti, C, and B powders. It is very difficult to densify these materials using conventional sintering techniques. It was found that the chemical reaction between the starting Titanium, boron and carbon particles could be completed at 1200°C producing a pure TiB 2 +TiC ceramic composite. Various carbon content causes the microstructure of the final products was different.