Polyolefin graft copolymers via living polymerization techniques: Preparation of poly(<i>n</i>‐butyl acrylate)‐<i>graft</i>‐polyethylene through the combination of Pd‐mediated living olefin polymerization and atom transfer radical polymerization

Abstract

Abstract Poly( n ‐butyl acrylate)‐ graft ‐branched polyethylene was successfully prepared by the combination of two living polymerization techniques. First, a branched polyethylene macromonomer with a methacrylate‐functionalized end group was prepared by Pd‐mediated living olefin polymerization. The macromonomer was then copolymerized with n ‐butyl acrylate by atom transfer radical polymerization. Gel permeation chromatography traces of the graft copolymers showed narrow molecular weight distributions indicative of a controlled reaction. At low macromonomer concentrations corresponding to low viscosities, the reactivity ratios of the macromonomer to n ‐butyl acrylate were similar to those for methyl methacrylate to n ‐butyl acrylate. However, the increased viscosity of the reaction solution resulting from increased macromonomer concentrations caused a lowering of the apparent reactivity ratio of the macromonomer to n ‐butyl acrylate, indicating an incompatibility between nonpolar polyethylene segments and a polar poly( n ‐butyl acrylate) backbone. The incompatibility was more pronounced in the solid state, exhibiting cylindrical nanoscale morphology as a result of microphase separation, as observed by atomic force microscopy. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 2736–2749, 2002