Polymer Engineering and Science · 2008 · 49 citations · 18 references
Natural SciencesMaterials EngineeringMaterials ScienceMaterials CharacterizationPolymer EngineeringPolymer MaterialsComposite MaterialsPolymer CharacterizationPolymer CrystallinityPolymer DegradationPolymer ProcessingPolymer StabilityCrystallinityCrystallinity ChangesCrystallinity Changes During AgingMicrostructural AlterationPolymer AgingPolypropyleneSecondary CrystallizationThermal Decomposition
Abstract The effects of elevated temperature aging on the microstructural changes of isotactic polypropylene matrix in a composite have been studied using wide‐angle X‐ray scattering (WAXS) and Fourier‐transform infrared spectroscopy (FTIR). The objective was to quantify small and slow changes in crystallinity due to thermal aging. To minimize sample variability, polypropylene resin was extracted from the molded composite plaque. Changes in crystallinity level and crystalline form were detected using WAXS after prolonged aging at 90 and 140°C. FTIR was utilized to monitor in‐situ crystallinity changes and to detect oxidation products due to thermal decomposition. The level of crystallinity was monitored by changes in the absorbance ratio of A 997 / A 973 and A 841 / A 973 ; the former ratio was found to be more sensitive for detecting crystallinity changes. Aging at 140°C resulted in oxidation. The kinetics of secondary crystallization for the aging conditions studied was characterized using Avrami plots. POLYM. ENG. SCI., 2008. © 2008 Society of Plastics Engineers
18