Piezoelectricity of a high-content lead zirconate titanate/polymer composite

Abstract

A binary system consisting of polyvinylidene fluoride (PVDF) and lead zirconate titanate (PZT) powder was investigated to determine its dielectric constant, piezoelectric constant, and Young’s modulus. An expression was obtained for the piezoelectric constant, and expressions for the dielectric constant and Young’s modulus were also mentioned. The calculated values had good agreement with the observed values for the composite with a large PZT volume fraction. The dielectric constant and the piezoelectric constant were 152 and 48.3×10−12 C/N, respectively, for the composite with the PZT volume fraction of 0.67. Changing the mixing ratio of PVDF and the fluorine elastomer, Young’s modulus was varied without changing the piezoelectric constant.