TSDC and DSC Study of Effects of Physical Aging on Polybutylene Terephthalate (PBT)

Abstract

The impact of the physical aging process on the electrical and thermal properties of semicrystalline polybutylene terephthalate (PBT) was investigated by means of thermally stimulated depolarization currents (TSDC) and differential scanning calorimetry (DSC). The TSDC technique was used to study the relaxation modes of PBT in the temperature range −50° to + 120°C. The obtained spectra revealed two peaks located at temperature maxima of 45° and 93°C. The peak appearing at 45°C corresponds to the dielectric manifestation of the glass transition phenomenon (α-relaxation). The aim of this work is to study the effect of physical aging on this relaxation. The recording of TSDC peaks of aged PBT at different temperatures for different times revealed a reduction in their intensities and their shift towards higher temperatures when the aging becomes significant. This result can be explained by the diminution of molecular chain mobility, which is directly related to the area under the peak representing the polarization of the sample. This result was confirmed by DSC measurements, which revealed the growth and the shift of the peak, which is superimposed on the jump of the heat capacity, located around 38°C and characteristic of the glass transition, towards higher temperatures where aging becomes significant.