Characterisation and sintering of nanophase hydroxyapatite synthesised by a species of<i>Serratia</i>

Abstract

The bacterium Serratia sp. NCIMB40259, which grows as a biofilm on polymeric, glass and metal substrates, produces extracellular crystals of hydroxyapatite (HA) by enzymatic cleavage of β-glycerophosphate in the presence of calcium chloride. Following growth on polyurethane foam, biomineralisation and subsequent sintering, an HA scaffold is formed whose three-dimensional architecture replicates that of the foam and the biofilm. Serratia HA was characterised using X-ray diffraction (XRD), Fourier Transform Infra-Red Spectroscopy (FTIR), energy dispersive X-ray analysis (EDX) scanning electron microscopy (SEM), transmission electron microscopy (TEM) and electron diffraction (ED). The nascent, unsintered material consisted mainly of calcium-deficient HA (CDHA) with a Ca/P ratio of 1.61+/- 0.06 and crystal size (TEM) of 50 +/- 10nm length. ED of unsintered crystals and crystals sintered at 600° C showed resolvable ring (unsintered) or dot (600° C) patterns ascribed to (0002), (1122) and (0006) planes of crystalline HA. Material sintered at 1200° C consisted of needle-like crystals of length range 54-111nm (XRD) with lattice parameters of a = 9.441 Å and c = 6.875 Å, consistent with HA.