Preparation of Ce‐doped TiO₂ Hollow Fibers and Their Photocatalytic Degradation Properties for Dye Compound

Abstract

Abstract Cerium‐doped titanium dioxide (TiO 2 ) with a hollow fiber structure was successfully prepared using ammonium ceric nitrate and tetrabutyltitanate as precursors and cotton fiber as the template. The effects of cerium (Ce)‐doping on the crystallite sizes, crystal pattern, and optical property of the prepared catalysts were investigated by means of techniques such as scanning electron microscopy (SEM), X‐ray diffraction (XRD), BET surface area, and UV‐vis diffuse absorption spectroscopy. SEM observation showed that the prepared TiO 2 fibers possessed fibrous shape inherited from the cotton fiber and had a hollow structure. As confirmed by XRD and UV‐vis diffuse absorption spectroscopy examinations, Ce‐doping restrained the growth of grain size and extended the photoabsorption edge of TiO 2 hollow fiber into the visible light region. The present photocatalyst showed higher photocatalytic reactivity in photodegradation of highly concentrated methylene blue (MB) solutions than pure TiO 2 under UV and visible light, and the amount of Ce‐doped significantly affected the catalytic property. In the experiment condition, the photocatalytic activity of 0.5 mol% Ce‐doped TiO 2 fiber was optimal of all the prepared samples. In addition, the possibility of cyclic usage of the photocatalyst was also confirmed. The material was easily removed by centrifugal separation. Therefore, using the template method and by doping with cerium, TiO 2 may hopefully become a low‐energy consuming, high activity and green environmentally friendly catalytic material.