IEEE Transactions on Magnetics · 1989 · 19 citations · 3 references
Natural SciencesMaterials SciencePhysicsCondensed Matter PhysicsMaterials PhysicsMetallic MaterialsElectrical ConductivityHigh-temperature MaterialsMetalsMicrowave MaterialsSuperconducting MaterialsSuperconducting Thin FilmsHigh-temperature Superconducting FilmsHigh-temperature SuperconductivityHigh-temperature SuperconductorsSuperconducting PropertiesSuperconducting Radiofrequency TechnologySurface ResistanceSurface Resistance Measurement
An investigation was conducted of the RF properties of high-T/sub c/ superconductors over a wide range of temperatures, frequencies and RF field amplitudes. Both bulk polycrystalline samples and thick films on silver substrates were tested. At 150 MHz and 4.2 K, surface resistances of 18 mu Omega at low RF field and 3.6 m Omega at an RF field of 270 G were measured. All samples showed a strong dependence of the surface resistance on RF field. However, no breakdown of the superconducting state was observed up to the highest field achieved (320 G).< <ETX xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">></ETX>
3
rf properties of an oxide-superconductor half-wave resonant line
Jean Delayen, K. C. Goretta, R.B. Poeppel et al. · Applied Physics Letters · 1988 · 38 citations