Toughening epoxy resins with polyepichlorohydrin

Abstract

Abstract Polyepichlorohydrin (PECH) rubbers were found to toughen epoxy resins based on the diglycidyl ether of bisphenol A (DGEBA) and cured with piperidine. The degree of toughening depends on the molecular weight of the PECH and on the curing temperature. Best toughening was achieved with PECH of the highest nominal molecular weight of 3400 (Hydrin 10 × 2). Hydrin 10 × 1 (nominal molecular weight 1700) did not toughen the epoxy resin unless bisphenol A was also added, whereas Hydrin 10 × 2 toughened it in the absence of bisphenol A. Curing resins containing bisphenol A and Hydrin 10 × 1 at 160°C resulted in a slightly more brittle resin than when cured at 120°C. The effect of PECH rubbers on the T g , modulus, and hot/wet properties is similar to that of carboxy‐terminated butadiene‐acrylonitrile rubbers (CTBN). Dynamic mechanical thermal analysis (DMTA) and scanning electron micrographs (SEM) of fractured surfaces show that the PECH separates as a discrete phase during curing. © 1993 John Wiley & Sons, Inc.