Bulk formation of a metallic glass: Pd40Ni40P20

Abstract

Molten spheroids of Pd40 Ni40 P20, of up to 0.53-cm minor diameter, were slowly cooled (1.4 K/s) on a fused silica surface under 10−6 Torr vacuum to a form which was entirely glassy except for some superficial crystallinity comprising less than 0.5% of the volume. The occurrence of crystallization was eliminated by subjecting the specimens to surface etching followed by a succession of heating and cooling cycles. The absence of crystallization in the bulk was confirmed by x-ray diffraction, transmission electron microscopy, and calorimetry. Using the last technique, the heat of crystallization of the glass was measured to be 5.3±0.3 kJ/g atom.