Enhancement of ferroelectric and magnetic properties in BiFeO3 films by small amount of cobalt addition

Abstract

Both the ferroelectric and magnetic properties of polycrystalline BiFeO3 films fabricated by chemical solution deposition were enhanced by adding small amounts of cobalt. Addition of 3at.% cobalt to BiFeO3 films increased the remanent polarization from 49to72μC∕cm2 and decreased the electric coercive field from 0.54to0.44MV∕cm. The ferroelectricity degraded when the cobalt concentration exceeded 9at.% due to the formation of the secondary phases of Bi2Pt. The saturation magnetization was drastically enhanced by the addition of cobalt up to 12at.%. This is because the magnetic moments are not canceled locally since the differences of magnetic moment between B-sites. The saturation magnetization decreased when the cobalt content exceeded 15at.%, thereby attributing to the formation of a nonmagnetic secondary phase of Bi2Pt. It is concluded that both ferroelectric and magnetic properties were enhanced, provided only small amount of cobalt were added to the films.