Magnetic Properties of UGaNi

Abstract

Measurements of susceptibility and magnetization in dependence on temperature and/or field are made on powder, polycrystalline, and single crystal samples of UGaNi. In the magnetic ordered state below 41 K, UGaNi yields magnetic relaxation with the value of the relaxation parameter τ = 6 min at 9 K. It is found that τp = 40.5 K, μeff = 1.9μB/formula unit and μs = 1.3,μB/formula unit. At 4.2 K the hysteresis loop of the polycrystalline sample is of perminvar (or waspwaisted) shape. After cooling in zero field the σ vs. T dependences of the polycrystalline and single crystal samples reveal the characteristic low field maximum. In UGaNi the c-axis is the direction of msy magnetization and the magnetic moment is probably localized on uranium. Messungeri der Suszeptibilität und Magnetisierung in Abhängigkeit von Temperntur und/oder Feld werden an Polykristall-, Einkristall- und Pulverproben von UGaNi durchgeführt. Im magnetisch geordneten Zustand unterhalb 41 Kzeigt UGaNi magnetische Relaxation mit einem Wert des Relaxntionsparameters τ = 6 min bei 9 K. Es wird gefunden, daß τp, = 40,5 K, μeff = 1,9μB/Formeleinheit und, μs = 1,3μB/Formeleinheit ist. Bei 4,2 K hat die Hysteresisschleife der polykristallinen Probe eine Perminvar- (oder Wespentaillen-) Form. Nach Abkühlung im Nullfeld zeigt die σ(T)-Abhängigkeit der Polykristall- und Einkristallproben das charakteristische Niederfeld-maximum. In UGaNi ist die c-Achse die Richtung der leichten Magnetisierbarkeit und das magnetische Moment ist wahrscheinlich am Uran lokalisiert.