Electric and magnetic properties of (B1−xLax)FeO3 solid solutions

Abstract

Results are reported on the electric and magnetic properties of (Bi1−xLax)FeO3 solid solution exhibiting simultaneously long-range order of electric and magnetic dipoles. In the concentration range 0 ≦ x < 0.30 close to the Néel temperature, an anomaly of ϵ(T) attributed to the influence of a decay of magnetic ordering on the electric ordering, was observed. A temperature-concentration phase diagram is constructed. Within the framework of Benguigui's theory [16], an explanation is proposed for the anomaly in electric properties at the transition boundaries between structural modifications. Ce travail contient les résultats d'une étude des propriétés électriques et magnétiques de la solution solide (Bi1−xLax)FeO3 présentant simultanément l'ordre lointain des dipǒles électriques et magnétiques. A des concentrations 0 ≦ x < 0,30 aux environs de la température de Néel, on a observé une anomalie de ϵ(T), attribuée à une influence sur l'ordre électrique de la part de la disparition d'ordre magnétique. Un diagramme de phases en fonction de la température et concentration est donné. A partir de la théorie de Benguigui [16], les causes des anomalies des propriétés électriques apparaissant aux limites entre les modifications structurelles sont expliquées.