Tunable long lasting phosphorescence due to the selective energy transfer from defects to luminescent centres via tunnelling in Mn2+ and Tm3+ co-doped zinc pyrophosphate

Abstract

A series of new phosphors Zn2(0.97-x)P2O7:0.06Tm(3+),2xMn(2+) (0 ≤ x ≤ 0.05) were synthesized and their luminescence properties were investigated. The results showed that the defects in all the phosphors were related to Tm(3+), and Mn(2+) merely served as the emission centres. Tm(3+) also acted as an emission centre and yielded blue phosphorescence corresponding to its characteristic f-f emissions in the phosphors where the Mn(2+) concentration was low (x ≤ 0.001), while in the phosphors with high concentrations of Mn(2+) it mainly served as a defect by forming Tm. The electrons thermally released from defects selectively transferred to Mn(2+) centres mainly through thermally-assisted tunnelling and this resulted in their red to near-infrared phosphorescence. By adjusting the ratio of Mn(2+) to Tm(3+) to control the spectral distribution, tunable long lasting phosphorescence from blue to near-infrared was achieved.