Solid⁷Li-NMR and<i>in situ</i>XRD studies of the insertion reaction of lithium with tin oxide and tin-based amorphous composite oxide

Abstract

The lithium insertion reactions with tin (II) oxide (SnO) and tin-based composite oxide (abbreviated as TBCO) are studied by solid 7Li-NMR Knight shift, T1 and T1ρ relaxation rate, TEM and in situ XRD methods. By the insertion reaction for SnO, the lithium oxide and β-tin are produced first at Li/Sn = 2; at Li/Sn = 3 to 6 the products are not simple and a mixture of LiSn2, LiSn, Li5Sn2 and Li7Sn2 alloys is detected during the insertion. For the TBCO, which is revealed as amorphous, mainly constituted by randomly distributed very short-range (order of 10-9 m) regions by TEM observation, it is found that electrochemically inserted lithium forms Li2O and produces metallic tin (Sn) in the first step (Li/Sn 2). During the second step, the Li/Sn ratio of formed lithium-tin alloy is kept at almost 4. By the analyses of 7Li NMR Knight shifts, line shape and in situ XRD, the lithium-inserted TBCOs are characterized as almost amorphous and mixtures of highly ionic components.