Influence of copper addition on electrical and optical properties of amorphous As2Se3

Abstract

Electrical conductivity and optical absorption of amorphous As2Se3: Cu are investigated as a function of the copper concentration up to 4 at%. Addition of copper up to 0.5 at% increases the density of localized tail states due to the increase of disorder. It is considered that at a copper content of 0.5 at% and more the Fermi level shifts toward the valence band, and that acceptor like states are produced. At a copper content of 1 at% and more, the optical energy gap decreases with the increase of copper concentration and an alloying effect is supposed to take place in the amorphous As2Se3. Die elektrische Leitakhigkeit und der optische Absorptionskoeffizient von amorphen As2Se3: Cu werden in Abhangigkeit vom Kupfergehalt bis zu 4 At% untersucht. Bei Zusatz von Kupfer biszu 0,5 At% nimmt die Dichte der lokalisierten Auslaufer-Zustande bedingt durch die Zunahme der Unordnung zu. Bei Kupfergehalt von 0,6 At% und daruber kann man annehmen, dast das Fermi - Niveau sich zum Valenzband hin verschiebt, und dast Akzeptor-ahnliche Zustinde erzeugt werden. Bei einem Kupfergehalt von 1 At% und daruber, nimmt die optische Energielucke mit zunehmender Kupferkonzentration ab und ein Legierungseffekt setzt im a- As2Se3 ein.