Over 7% magnetic field-induced strain in a Ni-Mn-Ga five-layered martensite

Abstract

A Ni-Mn-Ga single crystal with a modulated five-layered martensite structure is reported, demonstrating giant magnetic field induced strain (MFIS) of 7.1% at room temperature and of 6% at temperatures close to the austenite transformation (TA = 71 °C). The room temperature MFIS clearly exceeds the best results of around 6% measured earlier in 10M martensites. The larger MFIS is connected to the huge (>1%) change in the lattice distortion of the 10M structure, obtained within a narrow temperature interval of 47 K, which has been previously observed only during intermartensitic transformation. The present material shall effectively reduce the size of magnetic shape memory actuators.