Polymer thermoelectret dosimetry

Abstract

Radiation dosimetry based on thermoelectrets of nylon, mylar, polystyrene, and teflon is described. The effect of storage environment, forming temperature, and forming field strength have been examined for these four materials. The electret polarization was monitored by measuring the surface potential of the electrets by means of a contactless voltmeter probe. The electrets (except those of nylon) were found to be very stable under normal conditions. In the presence of X-ray or thermal neutron radiation they undergo a rapid and cumulative discharge. The total dosage received can be inferred from a comparison of the initial and residual polarizations. For 50 kV X-rays, a dosage of 1 mR is easily detectable by such measurements, and higher sensitivities are believed to be attainable in principle. Es werden Untersuchungen zur Strahlungsdosimetrie mit Hilfe von Thermoelektreten auf der Grundlage von Nylon, Mylar, Polystyrol und Teflon durchgeführt. Insbesondere wird der Einfluß der Lagerungsbedingungen, der Formierungstemperatur und der Formierungsfeldstärke studiert. Die Polarisation der Elektrete wurde durch Messung des Oberflächenpotentials unter Benutzung einer kontaktlosen Sonde verfolgt. Unter normalen Bedingungen erwiesen sich alle Substanzen außer Nylon als sehr stabil. Unter Einwirkung von Röntgenbestrahlung oder Bestrahlung mit thermischen Neutronen findet eine schnelle und sich steigernde Entladung statt. Die insgesamt aufgenommene Dosis kann durch Vergleich der anfänglichen und der Restpolarisation ermittelt werden. Für 50 kV-Röntgenstrahlung ist eine Dosis von 1 m durch derartige Messungen leicht nachweisbar, und es wird erwartet, daß noch höhere Empfindlichkeiten erreichbar sind.