Dynamic precipitation during multi-axial forging of an Mg–7Gd–5Y–1Nd–0.5Zr alloy

Abstract

The dynamic precipitation behavior during multi-axial forging in an Mg–7Gd–5Y–1Nd–0.5Zr alloy has been investigated and compared with that in static precipitation treatment. The results indicated that dynamic precipitation does occur during multi-axial forging. The dynamic precipitate can be deduced as β phase with face-centered cubic crystal structure (a = 2.22 nm). Most of the β precipitates locate at the dynamic recrystallization grain boundaries. The morphology and orientation relationship is different from that of the β phase formed in the static precipitation treated alloys, although the crystal structure is the same. The precipitation temperature of β phase during MAF is higher than that in the static precipitation treatment.