Temperature dependence of the sublattice magnetizations in Al- and Ga-substituted M-type hexagonal ferrites

Abstract

The Mössbauer absorption in BaFe12−xAlxO19, SrFe12−xGaxO19, and Ba1−ySryFe12−xAlxO19 compounds has been investigated. Measurements carried out at T < Tc allowed to determine the behaviour of the hyperfine magnetic fields of the Fe3+ ions in the five sublattices of these structures for some values of x as a function of T/Tc. The magnetization of the predominant K-sublattice, where six Fe3+ ions per unit formula are located, decreases more rapidly with increasing T/Tc for BaFe12O19and SrFe12O19 than for BaFe12−xAlxO19 and SrFe12−xGaxO19. This result demonstrates that the interactions between the octahedral sublattices with parallel magnetic moments appreciably influence the temperature dependence of the magnetization of the predominant sublattice. L'absorption Mössbauer a été étudié dans les composés BaFe12−xAlxO19, SrFe12−xGaxO19 et Ba1−ySryFe12−xAlxO19. Les mesures effectuées à T < Tc nous ont permis de déterminer la variation avec T/Tc pour des différent valeurs de x des champs internes dues aux ions Fe3+ repartis sur les cinque sousréseaux de ces structures. L'aimantation du sousréseau prédominant K, Où six ions Fe3+ par unité chimique sont placés, montre une diminution avec T/Tc plus rapide dans le cas du BaFe12O19 et SrFe12O19 que dans le cas du BaFe12−xAlxO19 et SrFe12−xGaxO19. Ce résultat montre que les interactions entre les sousréseaux octaédriques avec leur moments magnétiques parallèles ont une appréciable influence sur la dépendence de la température de l'aimantation du sousréseau principal.