Characterization of nanostructured spinel NiFe2O4 obtained by soft mechanochemical synthesis

Abstract

Powdery nickel ferrite, NiFe2O4 has been obtained by soft mechanochemical synthesis in a planetary ball mill. Ni(OH)2 and Fe(OH)3 are used as initial compounds. This mixture was mechanically activated for 25h, uniaxial pressed and sintered at 1100?C for 2h. The phase composition of the sintered sample was analyzed by X-ray diffraction (XRD), energy dispersive spectrometer (EDS) and Raman spectroscopy. Morphologies were examined by scanning electron microscopy (SEM). The electrical DC/resistivity/conductivity at different temperatures was measured using a Source Meter Keithley 2410. An Impedance/Gain-Phase Analyzer (HP-4194) was used to measure the impedance spectra (100Hz - 10MHz) at different temperatures.