Elastic properties of KCN and K(CN)1−xClx

Abstract

The elastic functions c11 and c44 of KCN are measured by the ultrasonic pulse-echo method and by Brillouin scattering in the cubic phase below room temperature and between 60 and 100 K in phases II and III. The elastic softening of c44 in the cubic phase can well be described by a linear strain—order parameter coupling. The same formalism explains the beginning softening of (c11—c12)/2, data of which are taken from the literature. It is shown that the interaction among CN groups is mediated by the lattice strain. Measurements of c44 in mixed crystals KCN/KCl indicate a strong shift of the stability limit of the cubic phase to lower values by replacing CN with Cl. Die elastischen Funktionen c11 and c44 von KCN werden mit Hilfe der Pulsechomethode und mittels Brillouinstreuung in der kubischen Phase unterhalb Zimmertemperatur sowie in den Phasen II und III zwischen 60 und 100 K gemessen. Das elastische Weichwerden von c44 läßt sich gut durch eine lineare Kopplung zwischen Deformation und Ordnungsparameter beschreiben. Der gleiche Formalismus erklärt das ebenfalls einsetzende Weichwerden von (c11 — c12)/2, wofür Daten der Literatur entnommen wurden. Es wird gezeigt, daß die Wechselwirkung zwischen den CN-Gruppen überwiegend durch die Deformation des Gitters vermittelt wird. Messungen von c44 an Mischkristallen KCN/KCl zeigen eine starke Verschiebung der Temperatur der Stabilitätsgrenze der kubischen Phase zu niedrigeren Werten, wenn CN durch Cl ersetzt wird.