Synthesis, characterization, and thermal properties of alternate copolymers containing <i>N,N</i>′‐bis(diphenylsilyl)tetraphenylcyclodisilazane

Abstract

Abstract Hexamethyldisilazane was used as the starting material to synthesize N , N ′‐bis(hydroxydiphenylsilanyl)tetraphenylcyclodisilazane (BHPTPC). By condensation polymerization of BHPTPC with α,ω‐bis(dialkylamino)dimethylsiloxane, a series of alternate copolymers containing N , N ′‐bis(diphenylsilyl)tetraphenylcyclodisilazane was synthesized. GPC studies show that the highest molecular weight was obtained at a ratio of 1.005 : 1 (BHPTPC: α,ω‐bis(dimethyl amino)dimethylsiloxane). Data of DSC indicate that the temperature of glass transition ( T g ) and temperature of melting point ( T m ) decreased with the increasing of dimethylsiloxane segments units. Three stages of degradation were found in the thermogravimetric analysis curves. The activation energy of the copolymer (with m = 2, 3, and 7) was calculated by using Flynn–Wall–Ozawa method. The activation energy of the copolymer with m = 2, 3, and 7 at second stage is 214, 211, and 184 kJ/mol, respectively. Isothermal gravimetric analysis shows that for the same temperature and the same time, the weight loss of the alternate copolymer was greatly less than that of common polydimethylsiloxane. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 103: 611–617, 2007