Dynamic Fatigue of a Machinable Glass‐Ceramic

Abstract

To assess the stress‐corrosion susceptibility of a machinable glass‐ceramic, its dynamic fatigue behavior was investigated by measuring its strength as a function of stress rate. Fracture mechanics techniques were used to analyze the results for the purpose of making lifetime predictions for components of this material. This material was concluded to have only moderate resistance ( N =30) to stress corrosion in ambient conditions. The effects of specimen size on strength were assessed for the material used in this study; it was concluded that the Weibull edge‐flaw scaling law adequately describes the observed strength‐size relation.